| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| CHS-EPOXY® 590 | BPF type | Modifications, adhesives, composites | 3,0-5,5 | 5,70-6,06 | 165-175 | max. 0,03 | max.100 |
ENVIPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| ENVIPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| ENVIPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| ENVIPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| CHS-EPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| CHS-EPOXY® 525 LA | BPA type with low α-glycol content | Modifications, adhesives, composites | 10,0-12,0 | 5,30-5,50 | 182-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| CHS-EPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| CHS-EPOXY® 590 | BPF type | Modifications, adhesives, composites | 3,0-5,5 | 5,70-6,06 | 165-175 | max. 0,03 | max.100 |
| CHS-EPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| CHS-EPOXY® 525 LA | BPA type with low α-glycol content | Modifications, adhesives, composites | 10,0-12,0 | 5,30-5,50 | 182-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| CHS-EPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| ENVIPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| ENVIPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| ENVIPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| ENVIPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 573 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 8,0-10,5 | 5,3-5,6 | 179-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 574 | BPA/F resin modified by difunctional reactive diluent | Composites, civil and electrical engineering, high-solid coatings | 1,4-1,7 | 5,5-5,75 | 174-182 | max. 0,1 | max.100 |
| CHS-EPOXY® 575 | BPA/F resin modified by difunctional reactive diluent | Solventless coatings, penetrants, filled systems, casting applications and insulating materials, high solid coatings | 0,7-0,9 | 5,6-5,9 | 169-179 | max. 0,1 | max.100 |
| CHS-EPOXY® 572 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 4,5-7,0 | 5,5-5,8 | 172-182 | max. 0,03 | max.100 |
| CHS-EPOXY® 514 | BPA/F resin modified by monofunctional reactive diluent | Composites, high solid, anticorrosion paints, civil engineering, casting | 0,8-1,1 | 5,1-5,4 | 185-196 | max. 0,1 | max.100 |
| CHS-EPOXY® 571 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 6,0-8,0 | 5,4-5,7 | 175-185 | max. 0,03 | max.100 |
| CHS-EPOXY® 619 | Epoxy resin modified with tri-functional reactive diluent | High performance laminating, potting, solventless coatings and impregnation | 0,4-0,9 | 5,9-6,5 | 155-170 | max. 0,2 | max.100 |
| CHS-EPOXY® 582 | Epoxy resin modified with bi-functional reactive diluent | Casting, composites, polymer concretes and mortans | 0,64-0,72 | 5,8-6,1 | 165-173 | max.100 | |
| CHS-EPOXY® 324 | Epoxy resin modified with a non-phthalate, non-reactive plasticizer | Adhesives for metals, wood, ceramics | 20,0-60,0 | 3,0-3,4 | 294-333 | max.300 | |
| CHS-EPOXY® 498 | Epoxy resin modified with mono-functional reactive diluent | Civil engineering, potting and impregnation | 0,5- 0,7 | 4,8-5,1 | 196-208 | max.100 | |
| CHS-EPOXY® 521 | Epoxy resin modified with mono-functional reactive diluent | Composites, potting, solventless coatings, civil engineering | 0,6-0,9 | 4,85-5,1 | 196-206 | max.100 | |
| CHS-EPOXY® 531 | Epoxy resin modified with bi-functional reactive diluent | Composites, solventless coatings and impregnations, construction (bonding agent for mortar, concrete and food industry compositions) | 1,5-2,3 | 5,5-5,7 | 175-182 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 619 | Epoxy resin modified with tri-functional reactive diluent | High performance laminating, potting, solventless coatings and impregnation | 0,4-0,9 | 5,9-6,5 | 155-170 | max. 0,2 | max.100 |
| CHS-EPOXY® 582 | Epoxy resin modified with bi-functional reactive diluent | Casting, composites, polymer concretes and mortans | 0,64-0,72 | 5,8-6,1 | 165-173 | max.100 | |
| CHS-EPOXY® 324 | Epoxy resin modified with a non-phthalate, non-reactive plasticizer | Adhesives for metals, wood, ceramics | 20,0-60,0 | 3,0-3,4 | 294-333 | max.300 | |
| CHS-EPOXY® 498 | Epoxy resin modified with mono-functional reactive diluent | Civil engineering, potting and impregnation | 0,5- 0,7 | 4,8-5,1 | 196-208 | max.100 | |
| CHS-EPOXY® 521 | Epoxy resin modified with mono-functional reactive diluent | Composites, potting, solventless coatings, civil engineering | 0,6-0,9 | 4,85-5,1 | 196-206 | max.100 | |
| CHS-EPOXY® 531 | Epoxy resin modified with bi-functional reactive diluent | Composites, solventless coatings and impregnations, construction (bonding agent for mortar, concrete and food industry compositions) | 1,5-2,3 | 5,5-5,7 | 175-182 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 573 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 8,0-10,5 | 5,3-5,6 | 179-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 574 | BPA/F resin modified by difunctional reactive diluent | Composites, civil and electrical engineering, high-solid coatings | 1,4-1,7 | 5,5-5,75 | 174-182 | max. 0,1 | max.100 |
| CHS-EPOXY® 575 | BPA/F resin modified by difunctional reactive diluent | Solventless coatings, penetrants, filled systems, casting applications and insulating materials, high solid coatings | 0,7-0,9 | 5,6-5,9 | 169-179 | max. 0,1 | max.100 |
| CHS-EPOXY® 572 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 4,5-7,0 | 5,5-5,8 | 172-182 | max. 0,03 | max.100 |
| CHS-EPOXY® 514 | BPA/F resin modified by monofunctional reactive diluent | Composites, high solid, anticorrosion paints, civil engineering, casting | 0,8-1,1 | 5,1-5,4 | 185-196 | max. 0,1 | max.100 |
| CHS-EPOXY® 571 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 6,0-8,0 | 5,4-5,7 | 175-185 | max. 0,03 | max.100 |
| Produkt | Description | Application | Viscosity (mPa) | Epoxy index | Hydrolysable chlorine | Colour (Gardner) |
|---|---|---|---|---|---|---|
| CHS-EPOXY® RR 800 | 1, 4-butanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | Oct-25 | 7,60-8,10 | max. 0,2 | max.1* |
| CHS-EPOXY® RR 690 | Trimethylol propane triglycidyl ether | Excellent mechanical strength and reactivity, hot water and solvent resistance, limited diluting power | 130-200 | 7,20-7,70 | max. 0,1 | max.1* |
| CHS-EPOXY® RR 330 | C12-C14 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 5-Oct | 2,94-3,70 | max. 0,1 | max.1* |
| CHS-EPOXY® RR 700 | 1, 6-hexanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 15-25 | 6,70-7,20 | max. 0,2 | max.1* |
| CHS-EPOXY® RR 300 | Polypropyleneglycol diglycidyl ether | Flexibilizer, low toxicity and vapour pressure, reduced reactivity, limited diluting power | 40-90 | 2,90-3,30 | max. 0,3 | max.2* |
| CHS-EPOXY® RR 430 | C8-C10 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 1-Jun | 4,25-4,55 | max. 0,05 | max.1* |
| TELALIT® 0600 | Cycloaliphatic, modified | High performance composites, long pot life, highest Tg | 80-100 | |||
| TELALIT® 0842 | Solvent free system, under water curing | Hardening in wet conditions, applicable in different weather conditions. | 1 100-1 900 | |||
| TELALIT® 0590 | Polyoxyetheramine | Composites, long pot life | 5-Oct | |||
| TELALIT® 0903 | Cycloaliphatic adduct modified | Self-levelling flooring, nonylphenol free, low yellowing | 200-500 | |||
| TELALIT® 1040 | Polyoxyetheramine | Waterborne coatings, high solid coatings, nonylphenol free. | Oct-30 | |||
| TELALIT® 0430 | Cycloaliphatic amine | Composites, civil engineering, faster curing, higher toughness | May-50 | |||
| TELALIT® 0492 | Cycloaliphatic modified | Composites, civil engineering | 15-30 | |||
| TELALIT® 0240 | Aliphatic amine (substitution for HARDENER P 11) | Standard, civil engineering, composites, adhesives | 5-Oct | |||
| TELALIT® 0500 | Cycloaliphatic amine | Composites, accelerated | May-50 | |||
| TELALIT® 0420 | Cycloaliphatic amine | Composites, higher Tg | Oct-25 |
| Produkt | Description | Application | Viscosity (mPa) | Amino number | HEW |
|---|---|---|---|---|---|
| TELALIT® 0600 | Cycloaliphatic, modified | High performance composites, long pot life, highest Tg | 80-100 | 450-500 | 62 |
| TELALIT® 0842 | Solvent free system, under water curing | Hardening in wet conditions, applicable in different weather conditions. | 1 100-1 900 | min.290 | 84 |
| TELALIT® 0590 | Polyoxyetheramine | Composites, long pot life | 5-Oct | 440-490 | 59 |
| TELALIT® 0903 | Cycloaliphatic adduct modified | Self-levelling flooring, nonylphenol free, low yellowing | 200-500 | 320-350 | 90 |
| TELALIT® 1040 | Polyoxyetheramine | Waterborne coatings, high solid coatings, nonylphenol free. | Oct-30 | 230-260 | 104 |
| TELALIT® 0430 | Cycloaliphatic amine | Composites, civil engineering, faster curing, higher toughness | May-50 | 1250-1320 | 43 |
| TELALIT® 0492 | Cycloaliphatic modified | Composites, civil engineering | 15-30 | 550-600 | 49 |
| TELALIT® 0240 | Aliphatic amine (substitution for HARDENER P 11) | Standard, civil engineering, composites, adhesives | 5-Oct | 24 | |
| TELALIT® 0500 | Cycloaliphatic amine | Composites, accelerated | May-50 | 1100-1200 | 50 |
| TELALIT® 0420 | Cycloaliphatic amine | Composites, higher Tg | Oct-25 | 600-650 | 42 |
| Produkt | Description | Application | Viscosity (mPa) | Epoxy index | Hydrolysable chlorine | Colour (Gardner) |
|---|---|---|---|---|---|---|
| CHS-EPOXY® RR 800 | 1, 4-butanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | Oct-25 | 7,60-8,10 | max. 0,2 | max.1* |
| CHS-EPOXY® RR 690 | Trimethylol propane triglycidyl ether | Excellent mechanical strength and reactivity, hot water and solvent resistance, limited diluting power | 130-200 | 7,20-7,70 | max. 0,1 | max.1* |
| CHS-EPOXY® RR 330 | C12-C14 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 5-Oct | 2,94-3,70 | max. 0,1 | max.1* |
| CHS-EPOXY® RR 700 | 1, 6-hexanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 15-25 | 6,70-7,20 | max. 0,2 | max.1* |
| CHS-EPOXY® RR 300 | Polypropyleneglycol diglycidyl ether | Flexibilizer, low toxicity and vapour pressure, reduced reactivity, limited diluting power | 40-90 | 2,90-3,30 | max. 0,3 | max.2* |
| CHS-EPOXY® RR 430 | C8-C10 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 1-Jun | 4,25-4,55 | max. 0,05 | max.1* |
| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life | Shear strength |
|---|---|---|---|---|---|---|
| VEROBOND® 520-2608 | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/140 | 70-80 | 20 min/25°C/50g | 20-25 |
| VEROBOND® SUPER | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/100 | 70-80 | 20 min/25°C/10g | 20-24 |
| VEROBOND® QUICK | Unique, very fast epoxy adhesive (5 minutes curing time). | A/B | 100/100 | 50-60 | 3 min/25°C/10g | 10-Dec |
| VEROBOND® 14 | Epoxy adhesive cured at room temperature. Systems is a thixotropic paste of high strength with good chemical resistance. | A/B | 100/50 | 80-85 | 60 min/25°C/100g | 20-24 |
| VEROBOND® 521-0846 | Two-component epoxy structural adhesive. It is used for structural bonding of a wide range of substrates, especially metals, metal structures, wood and ceramics. | A/B | 100/50 | 60-70 | 28 min/25°C/15g | 6-Aug |
| VEROBOND® 15 | Hybrid epoxy structural adhesive with high elongation and excellent peel and shear strengths. | A/B | 100/100 | 60-70 | 25 min/25°C/100g | 20-24 |
| VEROBOND® 531-0903 | Epoxy adhesive with low viscosity, cured at room temperature. Optimal for chemical anchors. | A/B | 100/50 | 50-60 | 35 min/25°C/400g | 15-20 |
| CHS-EPODUR® 574-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, medium viscosity, fast to slow reactivity. Optimal for hand lay-up. | A/B | 100/28 (34) | 90-115 (65) | 0.3-4 h/25°C | |
| CHS-EPODUR® 582-0420 | Medium reactivity, low viscosity, high mechanical properties. | A/B | 100/25 | 120-130 | 0.5-1 h/25°C | |
| CHS-EPODUR® 581-0542/0562 | Combination of one resin with two hardeners, low viscosity, fast to slow reactivity. Optimal for wind mill blades. | A/B | 100/32 | 80-85 | 1-2 h/25°C | |
| CHS-EPODUR® 582-0600 | Slow reactivity, low viscosity, high mechanical properties. | A/B | 100/37 | 130-150 | 2-3 h/25°C | |
| CHS-EPODUR® 582-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, low viscosity, fast to slow reactivity. Optimal for infusion. | A/B | 100/30 (36) | 90-115 (65) | 0.3-4 h/25°C |
| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life | Viscosity (mPa.s) |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 574-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, medium viscosity, fast to slow reactivity. Optimal for hand lay-up. | A/B | 100/28 (34) | 90-115 (65) | 0.3-4 h/25°C | 350-650 //5 |
| CHS-EPODUR® 582-0420 | Medium reactivity, low viscosity, high mechanical properties. | A/B | 100/25 | 120-130 | 0.5-1 h/25°C | 300-450 //5 |
| CHS-EPODUR® 581-0542/0562 | Combination of one resin with two hardeners, low viscosity, fast to slow reactivity. Optimal for wind mill blades. | A/B | 100/32 | 80-85 | 1-2 h/25°C | 200-250 //5 |
| CHS-EPODUR® 582-0600 | Slow reactivity, low viscosity, high mechanical properties. | A/B | 100/37 | 130-150 | 2-3 h/25°C | 350-550 //5 |
| CHS-EPODUR® 582-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, low viscosity, fast to slow reactivity. Optimal for infusion. | A/B | 100/30 (36) | 90-115 (65) | 0.3-4 h/25°C | 200-400 //5 |
| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life | Shear strength |
|---|---|---|---|---|---|---|
| VEROBOND® 520-2608 | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/140 | 70-80 | 20 min/25°C/50g | 20-25 |
| VEROBOND® SUPER | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/100 | 70-80 | 20 min/25°C/10g | 20-24 |
| VEROBOND® QUICK | Unique, very fast epoxy adhesive (5 minutes curing time). | A/B | 100/100 | 50-60 | 3 min/25°C/10g | 10-Dec |
| VEROBOND® 14 | Epoxy adhesive cured at room temperature. Systems is a thixotropic paste of high strength with good chemical resistance. | A/B | 100/50 | 80-85 | 60 min/25°C/100g | 20-24 |
| VEROBOND® 521-0846 | Two-component epoxy structural adhesive. It is used for structural bonding of a wide range of substrates, especially metals, metal structures, wood and ceramics. | A/B | 100/50 | 60-70 | 28 min/25°C/15g | 6-Aug |
| VEROBOND® 15 | Hybrid epoxy structural adhesive with high elongation and excellent peel and shear strengths. | A/B | 100/100 | 60-70 | 25 min/25°C/100g | 20-24 |
| VEROBOND® 531-0903 | Epoxy adhesive with low viscosity, cured at room temperature. Optimal for chemical anchors. | A/B | 100/50 | 50-60 | 35 min/25°C/400g | 15-20 |
You can also find a comprehensive range of products in the product catalogue (PDF).
If you require detailed product information, please do not hesitate to contact us.