| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life | Viscosity (mPa.s) |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C | 1 000-1 200 //5 |
| CHS-EPODUR® 520-1687 | Long pot life, low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90/1 | 130-145 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 574-0904 | Laminated system with medium viscosity. High adhesion to dural, steel and other metal surfaces. | A/B | 100/50 | 70-80 | 12-15 min/25°C | 1 600-2 200 //5 |
| CHS-EPODUR® 520-1667 | Low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0.5/10 | 85-95 | > 10 h/25°C | 1 500-2 000 //5 |
| CHS-EPODUR® 574-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, medium viscosity, fast to slow reactivity. Optimal for hand lay-up. | A/B | 100/28 (34) | 90-115 (65) | 0.3-4 h/25°C | 350-650 //5 |
| CHS-EPODUR® 619-0492 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/32 | 80-90 | 12-30 min/25°C | 200-500 //5 |
| CHS-EPODUR® 582-0420 | Medium reactivity, low viscosity, high mechanical properties. | A/B | 100/25 | 120-130 | 0.5-1 h/25°C | 300-450 //5 |
| CHS-EPODUR® 581-0542/0562 | Combination of one resin with two hardeners, low viscosity, fast to slow reactivity. Optimal for wind mill blades. | A/B | 100/32 | 80-85 | 1-2 h/25°C | 200-250 //5 |
| CHS-EPODUR® 621-0600 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/40 | 115-130 | 0.5-1 h/25°C | 500-800 //5 |
| CHS-EPODUR® 619-0600 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/40 | 115-130 | 2-3 h/25°C | 200-500 //5 |
| CHS-EPODUR® 582-0600 | Slow reactivity, low viscosity, high mechanical properties. | A/B | 100/37 | 130-150 | 2-3 h/25°C | 350-550 //5 |
| CHS-EPODUR® 621-0492 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. | A/B | 100/32 | 85-100 | 20-40 min/25°C | 300-500 //5 |
| CHS-EPODUR® 582-0512/0492/0502/0482/0590 | Combination of one resin with five hardeners, low viscosity, fast to slow reactivity. Optimal for infusion. | A/B | 100/30 (36) | 90-115 (65) | 0.3-4 h/25°C | 200-400 //5 |
| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life |
|---|---|---|---|---|---|
| CHS-EPODUR® 525-0269 | Solvent-free epoxy prepregging system with chemically induced B-stage, adjustable tack/ drapability. For cold, simple equipped processing. Recommended for general industrial and sport & leisure applications. | A/B/C55 | 100/12/0-3 | 115 - 135 | 2 - 8 h //12 |
| CHS-EPODUR® 411-0269 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack. For industrial and sport & leisure composite applications. | A/B/C55 | 100/9/0-2 | 120 - 128 | 0,5 - 2 h //12 |
| CHS-EPODUR® N 554-0249 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack/drapability. For applications with higher temperature resistance. | A/B/C55 | 100/10/0-3 | 120 - 165 | 1 - 4 h //12 |
| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life | Viscosity (mPa.s) |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 520-1687 | Long pot life, medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90 /1 | 130-145 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1667 | Medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C | 1 000-1 200 //5 |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0,5/10 | 85-95 | > 10 h/25°C | 1 500-2 000 //5 |
| CHS-EPODUR® 574-0522 | Curing at ambient temperature, slow reactivity. | A/B | 100/30 | 85-100 | 1-2 h/25°C | 200-500 //5 |
| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life | Shear strength |
|---|---|---|---|---|---|---|
| VEROBOND® 520-2608 | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/140 | 70-80 | 20 min/25°C/50g | 20-25 |
| VEROBOND® SUPER | Structural adhesive with high elongation up to 55% with excellent peel and shear strength. | A/B | 100/100 | 70-80 | 20 min/25°C/10g | 20-24 |
| VEROBOND® QUICK | Unique, very fast epoxy adhesive (5 minutes curing time). | A/B | 100/100 | 50-60 | 3 min/25°C/10g | 10-Dec |
| VEROBOND® 14 | Epoxy adhesive cured at room temperature. Systems is a thixotropic paste of high strength with good chemical resistance. | A/B | 100/50 | 80-85 | 60 min/25°C/100g | 20-24 |
| VEROBOND® 521-0846 | Two-component epoxy structural adhesive. It is used for structural bonding of a wide range of substrates, especially metals, metal structures, wood and ceramics. | A/B | 100/50 | 60-70 | 28 min/25°C/15g | 6-Aug |
| VEROBOND® 15 | Hybrid epoxy structural adhesive with high elongation and excellent peel and shear strengths. | A/B | 100/100 | 60-70 | 25 min/25°C/100g | 20-24 |
| VEROBOND® 531-0903 | Epoxy adhesive with low viscosity, cured at room temperature. Optimal for chemical anchors. | A/B | 100/50 | 50-60 | 35 min/25°C/400g | 15-20 |
You can also find a comprehensive range of products in the product catalogue (PDF).
If you require detailed product information, please do not hesitate to contact us.