| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life | Viscosity (mPa.s) |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C | 1 000-1 200 //5 |
| CHS-EPODUR® 520-1687 | Long pot life, low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90/1 | 130-145 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 574-0904 | Laminated system with medium viscosity. High adhesion to dural, steel and other metal surfaces. | A/B | 100/50 | 70-80 | 12-15 min/25°C | 1 600-2 200 //5 |
| CHS-EPODUR® 520-1667 | Low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0.5/10 | 85-95 | > 10 h/25°C | 1 500-2 000 //5 |
| CHS-EPODUR® 525-0269 | Solvent-free epoxy prepregging system with chemically induced B-stage, adjustable tack/ drapability. For cold, simple equipped processing. Recommended for general industrial and sport & leisure applications. | A/B/C55 | 100/12/0-3 | 115 - 135 | 2 - 8 h //12 | |
| CHS-EPODUR® 411-0269 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack. For industrial and sport & leisure composite applications. | A/B/C55 | 100/9/0-2 | 120 - 128 | 0,5 - 2 h //12 | |
| CHS-EPODUR® N 554-0249 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack/drapability. For applications with higher temperature resistance. | A/B/C55 | 100/10/0-3 | 120 - 165 | 1 - 4 h //12 | |
| CHS-EPODUR® 520-1687 | Long pot life, medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90 /1 | 130-145 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1667 | Medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C | 1 000-1 200 //5 |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0,5/10 | 85-95 | > 10 h/25°C | 1 500-2 000 //5 |
| CHS-EPODUR® 574-0522 | Curing at ambient temperature, slow reactivity. | A/B | 100/30 | 85-100 | 1-2 h/25°C | 200-500 //5 |
| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life | Viscosity (mPa.s) |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C | 1 000-1 200 //5 |
| CHS-EPODUR® 520-1687 | Long pot life, low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90/1 | 130-145 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 574-0904 | Laminated system with medium viscosity. High adhesion to dural, steel and other metal surfaces. | A/B | 100/50 | 70-80 | 12-15 min/25°C | 1 600-2 200 //5 |
| CHS-EPODUR® 520-1667 | Low viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0.5/10 | 85-95 | > 10 h/25°C | 1 500-2 000 //5 |
| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life |
|---|---|---|---|---|---|
| CHS-EPODUR® 525-0269 | Solvent-free epoxy prepregging system with chemically induced B-stage, adjustable tack/ drapability. For cold, simple equipped processing. Recommended for general industrial and sport & leisure applications. | A/B/C55 | 100/12/0-3 | 115 - 135 | 2 - 8 h //12 |
| CHS-EPODUR® 411-0269 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack. For industrial and sport & leisure composite applications. | A/B/C55 | 100/9/0-2 | 120 - 128 | 0,5 - 2 h //12 |
| CHS-EPODUR® N 554-0249 | Solvent-free epoxy system for hot-melt prepregging, adjustable tack/drapability. For applications with higher temperature resistance. | A/B/C55 | 100/10/0-3 | 120 - 165 | 1 - 4 h //12 |
| Produkt | Description | Components | Mixing ratio | Tg, DSC | Pot-life | Viscosity (mPa.s) |
|---|---|---|---|---|---|---|
| CHS-EPODUR® 520-1687 | Long pot life, medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/90 /1 | 130-145 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1667 | Medium viscosity. Curing at higher temperature (at least 80°C). | A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C | 500-1 000 //5 |
| CHS-EPODUR® 520-1997 | High thermal resistance. Post curing above 160°C. | A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C | 1 000-1 200 //5 |
| CHS-EPODUR® 520-1787 | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | A/B/C1/D1 | 100/85/0,5/10 | 85-95 | > 10 h/25°C | 1 500-2 000 //5 |
| CHS-EPODUR® 574-0522 | Curing at ambient temperature, slow reactivity. | A/B | 100/30 | 85-100 | 1-2 h/25°C | 200-500 //5 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 573 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 8,0-10,5 | 5,3-5,6 | 179-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 574 | BPA/F resin modified by difunctional reactive diluent | Composites, civil and electrical engineering, high-solid coatings | 1,4-1,7 | 5,5-5,75 | 174-182 | max. 0,1 | max.100 |
| CHS-EPOXY® 575 | BPA/F resin modified by difunctional reactive diluent | Solventless coatings, penetrants, filled systems, casting applications and insulating materials, high solid coatings | 0,7-0,9 | 5,6-5,9 | 169-179 | max. 0,1 | max.100 |
| CHS-EPOXY® 572 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 4,5-7,0 | 5,5-5,8 | 172-182 | max. 0,03 | max.100 |
| CHS-EPOXY® 514 | BPA/F resin modified by monofunctional reactive diluent | Composites, high solid, anticorrosion paints, civil engineering, casting | 0,8-1,1 | 5,1-5,4 | 185-196 | max. 0,1 | max.100 |
| CHS-EPOXY® 571 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 6,0-8,0 | 5,4-5,7 | 175-185 | max. 0,03 | max.100 |
| CHS-EPOXY® 501 | BPA/F resin modified by monofunctional reactive diluent | Composites, high solid, anticorrosion paints, civil engineering, casting | 0,6-0,8 | 5,0-5,3 | 188-200 | max. 0,1 | max.100 |
| CHS-EPOXY® 582 | Epoxy resin modified with bi-functional reactive diluent | Casting, composites, polymer concretes and mortans | 0,64-0,72 | 5,8-6,1 | 165-173 | max.100 | |
| CHS-EPOXY® 324 | Epoxy resin modified with a non-phthalate, non-reactive plasticizer | Adhesives for metals, wood, ceramics | 20,0-60,0 | 3,0-3,4 | 294-333 | max.300 | |
| CHS-EPOXY® 498 | Epoxy resin modified with mono-functional reactive diluent | Civil engineering, potting and impregnation | 0,5- 0,7 | 4,8-5,1 | 196-208 | max.100 | |
| CHS-EPOXY® 455 | Epoxy resin modified with a non-phthalate, non-reactive plasticizer | Adhesives, civil engineering and composites | 2,0-4,0 | 4,3-4,8 | 208-232 | max.100 | |
| CHS-EPOXY® 521 | Epoxy resin modified with mono-functional reactive diluent | Composites, potting, solventless coatings, civil engineering | 0,6-0,9 | 4,85-5,1 | 196-206 | max.100 | |
| CHS-EPOXY® 512 | Epoxy resin modified with non-reactive modifier, flexibilized | Casting, composites, adhesives, construction (bonding agent for mortar, concrete and high chemical resistance compositions) | 2,5-4,1 | 4,3-4,8 | 208-233 | max.100 | |
| CHS-EPOXY® 474 | Epoxy resin modified with mono-functional reactive diluent | Composites, coatings, applications in civil engineering, casting compounds | 0,3-0,6 | 4,5-4,9 | 204-223 | max.100 | |
| CHS-EPOXY® 531 | Epoxy resin modified with bi-functional reactive diluent | Composites, solventless coatings and impregnations, construction (bonding agent for mortar, concrete and food industry compositions) | 1,5-2,3 | 5,5-5,7 | 175-182 | max.100 | |
| CHS-EPOXY® 517 | Epoxy resin modified with reactive diluent, flexibilized | Casting, composites, adhesives, construction (bonding agent for mortar and concrete) | 0,55-0,95 | 4,3-4,7 | 213-233 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Colour (APHA) |
|---|---|---|---|---|---|---|
| CHS-EPOXY® 582 | Epoxy resin modified with bi-functional reactive diluent | Casting, composites, polymer concretes and mortans | 0,64-0,72 | 5,8-6,1 | 165-173 | max.100 |
| CHS-EPOXY® 324 | Epoxy resin modified with a non-phthalate, non-reactive plasticizer | Adhesives for metals, wood, ceramics | 20,0-60,0 | 3,0-3,4 | 294-333 | max.300 |
| CHS-EPOXY® 498 | Epoxy resin modified with mono-functional reactive diluent | Civil engineering, potting and impregnation | 0,5- 0,7 | 4,8-5,1 | 196-208 | max.100 |
| CHS-EPOXY® 455 | Epoxy resin modified with a non-phthalate, non-reactive plasticizer | Adhesives, civil engineering and composites | 2,0-4,0 | 4,3-4,8 | 208-232 | max.100 |
| CHS-EPOXY® 521 | Epoxy resin modified with mono-functional reactive diluent | Composites, potting, solventless coatings, civil engineering | 0,6-0,9 | 4,85-5,1 | 196-206 | max.100 |
| CHS-EPOXY® 512 | Epoxy resin modified with non-reactive modifier, flexibilized | Casting, composites, adhesives, construction (bonding agent for mortar, concrete and high chemical resistance compositions) | 2,5-4,1 | 4,3-4,8 | 208-233 | max.100 |
| CHS-EPOXY® 474 | Epoxy resin modified with mono-functional reactive diluent | Composites, coatings, applications in civil engineering, casting compounds | 0,3-0,6 | 4,5-4,9 | 204-223 | max.100 |
| CHS-EPOXY® 531 | Epoxy resin modified with bi-functional reactive diluent | Composites, solventless coatings and impregnations, construction (bonding agent for mortar, concrete and food industry compositions) | 1,5-2,3 | 5,5-5,7 | 175-182 | max.100 |
| CHS-EPOXY® 517 | Epoxy resin modified with reactive diluent, flexibilized | Casting, composites, adhesives, construction (bonding agent for mortar and concrete) | 0,55-0,95 | 4,3-4,7 | 213-233 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 573 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 8,0-10,5 | 5,3-5,6 | 179-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 574 | BPA/F resin modified by difunctional reactive diluent | Composites, civil and electrical engineering, high-solid coatings | 1,4-1,7 | 5,5-5,75 | 174-182 | max. 0,1 | max.100 |
| CHS-EPOXY® 575 | BPA/F resin modified by difunctional reactive diluent | Solventless coatings, penetrants, filled systems, casting applications and insulating materials, high solid coatings | 0,7-0,9 | 5,6-5,9 | 169-179 | max. 0,1 | max.100 |
| CHS-EPOXY® 572 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 4,5-7,0 | 5,5-5,8 | 172-182 | max. 0,03 | max.100 |
| CHS-EPOXY® 514 | BPA/F resin modified by monofunctional reactive diluent | Composites, high solid, anticorrosion paints, civil engineering, casting | 0,8-1,1 | 5,1-5,4 | 185-196 | max. 0,1 | max.100 |
| CHS-EPOXY® 571 | BPA/F epoxy resin | Coatings, penetrants, filled systems, casting applications and insulating materials | 6,0-8,0 | 5,4-5,7 | 175-185 | max. 0,03 | max.100 |
| CHS-EPOXY® 501 | BPA/F resin modified by monofunctional reactive diluent | Composites, high solid, anticorrosion paints, civil engineering, casting | 0,6-0,8 | 5,0-5,3 | 188-200 | max. 0,1 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| CHS-EPOXY® 590 | BPF type | Modifications, adhesives, composites | 3,0-5,5 | 5,70-6,06 | 165-175 | max. 0,03 | max.100 |
ENVIPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| ENVIPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| ENVIPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| ENVIPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| CHS-EPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| CHS-EPOXY® 525 LA | BPA type with low α-glycol content | Modifications, adhesives, composites | 10,0-12,0 | 5,30-5,50 | 182-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| CHS-EPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| CHS-EPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| CHS-EPOXY® 590 | BPF type | Modifications, adhesives, composites | 3,0-5,5 | 5,70-6,06 | 165-175 | max. 0,03 | max.100 |
| CHS-EPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| CHS-EPOXY® 525 LA | BPA type with low α-glycol content | Modifications, adhesives, composites | 10,0-12,0 | 5,30-5,50 | 182-189 | max. 0,03 | max.100 |
| CHS-EPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| CHS-EPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| Produkt | Description | Application | Viscosity (Pa) | Epoxy index | EEW | Hydrolysable chlorine | Colour (APHA) |
|---|---|---|---|---|---|---|---|
| ENVIPOXY® 525 | BPA type | Modifications, adhesives, composites | 10,0-12,0 | 5,29-5,59 | 179-189 | max. 0,03 | max.100 |
| ENVIPOXY® 510 | BPA type, low tendency to crystallize | Modifications, adhesives, composites | 12,5-16,0 | 5,18-5,46 | 183-193 | max. 0,03 | max.200 |
| ENVIPOXY® 530 | BPA type | Modifications, adhesives, composites | 8,0-10,0 | 5,38-5,68 | 176-186 | max. 0,03 | max.100 |
| ENVIPOXY® 520 | BPA type | Modifications, adhesives, composites | 12,0-14,5 | 5,21-5,50 | 182-192 | max. 0,03 | max.100 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
EPOSTYL® 200 V | Waterborne epoxy dispersion | Glossy topcoat for interior applications on wood, concrete and metal | A/B | 100/26 //6 |
| EPOSTYL® 521-01 | Solvent-free epoxy system. Different colours upon request (based on RAL). | Coloured coating system with higher UV resistance | A/B | 100/30 |
| EPOSTYL® 200 V MAT | Waterborne matt coating | Matt topcoat for flooring, parquets and other surfaces | A/B | 100/21 //6 |
| EPOSTYL® 200 V MAT | Waterborne matt coating | Matt top coat for flooring, parquets and other surfaces | A/B | 100/21 //6 |
| CHS-EPODUR® 474 PRIMER | Low viscosity epoxy system, penetration, adhesion and water control insulation | Bonding agent, primer for bridges, roads, pavements, flooring | A/B | 100/23 |
| EPOSTYL® 200 V | Waterborne epoxy dispersion | Primer/penetrating sealer | A/B | 100/26 //6 |
| CHS-EPODUR® 474 PRIMER FAST | Low viscosity epoxy system, for use at lower temperature | Bonding agent, primer | A/B | 100/40 |
| CHS-EPOSTYL® 521-2433 | Solvent-free water-based epoxy system | Primer/penetrating sealer | A/B | 100/140 //6 |
| SADURIT® Z 1 | Solvent based epoxy system. Different colours upon request (based on RAL). | Coloured coating systems, high mechanical & chemical resistance, interior/exterior | A/B | 100/25 |
| EPOSTYL® 215 V | Waterborne epoxy system. Different colours upon request (based on RAL). | Matt topcoat system for concrete, usable in poorly ventilated rooms, vapour permeable | A/B | 100/14 //6 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
| CHS-EPODUR® 474 PRIMER | Low viscosity epoxy system, penetration, adhesion and water control insulation | Bonding agent, primer for bridges, roads, pavements, flooring | A/B | 100/23 |
| EPOSTYL® 200 V | Waterborne epoxy dispersion | Primer/penetrating sealer | A/B | 100/26 //6 |
| CHS-EPODUR® 474 PRIMER FAST | Low viscosity epoxy system, for use at lower temperature | Bonding agent, primer | A/B | 100/40 |
| CHS-EPOSTYL® 521-2433 | Solvent-free water-based epoxy system | Primer/penetrating sealer | A/B | 100/140 //6 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
| EPOSTYL® 521-01 | Solvent-free epoxy system. Different colours upon request (based on RAL). | Coloured coating system with higher UV resistance | A/B | 100/30 |
| EPOSTYL® 200 V MAT | Waterborne matt coating | Matt top coat for flooring, parquets and other surfaces | A/B | 100/21 //6 |
| SADURIT® Z 1 | Solvent based epoxy system. Different colours upon request (based on RAL). | Coloured coating systems, high mechanical & chemical resistance, interior/exterior | A/B | 100/25 |
| EPOSTYL® 215 V | Waterborne epoxy system. Different colours upon request (based on RAL). | Matt topcoat system for concrete, usable in poorly ventilated rooms, vapour permeable | A/B | 100/14 //6 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
| EPOSTYL® 200 V | Waterborne epoxy dispersion | Glossy topcoat for interior applications on wood, concrete and metal | A/B | 100/26 //6 |
| EPOSTYL® 200 V MAT | Waterborne matt coating | Matt topcoat for flooring, parquets and other surfaces | A/B | 100/21 //6 |
| Produkt | Description | Application | Viscosity (mPa) | Epoxy index | Hydrolysable chlorine | Colour (Gardner) |
|---|---|---|---|---|---|---|
| CHS-EPOXY® RR 800 | 1, 4-butanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | Oct-25 | 7,60-8,10 | max. 0,2 | max.1* |
| TELALIT® 2433 VBG 50 | Polyamine adduct modified (substitution for TELALIT® 180) | Waterborne systems | 1000-2000 | |||
| CHS-EPOXY® RR 690 | Trimethylol propane triglycidyl ether | Excellent mechanical strength and reactivity, hot water and solvent resistance, limited diluting power | 130-200 | 7,20-7,70 | max. 0,1 | max.1* |
| TELALIT® 95 | Cycloaliphatic adduct modified | Self-levelling flooring | 170-400 | |||
| CHS-EPOXY® RR 330 | C12-C14 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 5-Oct | 2,94-3,70 | max. 0,1 | max.1* |
| CHS-EPOXY® RR 700 | 1, 6-hexanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 15-25 | 6,70-7,20 | max. 0,2 | max.1* |
| CHS-EPOXY® RR 300 | Polypropyleneglycol diglycidyl ether | Flexibilizer, low toxicity and vapour pressure, reduced reactivity, limited diluting power | 40-90 | 2,90-3,30 | max. 0,3 | max.2* |
| CHS-EPOXY® RR 430 | C8-C10 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 1-Jun | 4,25-4,55 | max. 0,05 | max.1* |
| TELALIT® 0600 | Cycloaliphatic, modified | High performance composites, long pot life, highest Tg | 80-100 | |||
| TELALIT® 0842 | Solvent free system, under water curing | Hardening in wet conditions, applicable in different weather conditions. | 1 100-1 900 | |||
| TELALIT® 0590 | Polyoxyetheramine | Composites, long pot life | 5-Oct | |||
| TELALIT® 0846 | Mannich base without phenol (substitution for TELALIT® 60) | Universal hardener for epoxy systems, applicable in lower temperatures, unsuitable for food, beverages and drinking water | 550-750 | |||
| TELALITE® 1203 NF | Cycloaliphatic adduct, modified | For high solid coatings, nonyl phenol free | 50-400 | |||
| TELALIT® 0903 | Cycloaliphatic adduct modified | Self-levelling flooring, nonylphenol free, low yellowing | 200-500 | |||
| TELALIT® 3509 IX 50 | Aliphatic adduct modified (substitution for TELALIT® 160) | Lacquers, anticorrosive coatings | 200-700 | |||
| TELALIT® 1040 | Polyoxyetheramine | Waterborne coatings, high solid coatings, nonylphenol free. | Oct-30 | |||
| TELALIT® 0430 | Cycloaliphatic amine | Composites, civil engineering, faster curing, higher toughness | May-50 | |||
| TELALIT® 0492 | Cycloaliphatic modified | Composites, civil engineering | 15-30 | |||
| TELALIT® 0240 | Aliphatic amine (substitution for HARDENER P 11) | Standard, civil engineering, composites, adhesives | 5-Oct | |||
| TELALIT® 0500 | Cycloaliphatic amine | Composites, accelerated | May-50 | |||
| TELALIT® 0420 | Cycloaliphatic amine | Composites, higher Tg | Oct-25 |
| Produkt | Description | Application | Viscosity (mPa) | Epoxy index | Hydrolysable chlorine | Colour (Gardner) |
|---|---|---|---|---|---|---|
| CHS-EPOXY® RR 800 | 1, 4-butanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | Oct-25 | 7,60-8,10 | max. 0,2 | max.1* |
| CHS-EPOXY® RR 690 | Trimethylol propane triglycidyl ether | Excellent mechanical strength and reactivity, hot water and solvent resistance, limited diluting power | 130-200 | 7,20-7,70 | max. 0,1 | max.1* |
| CHS-EPOXY® RR 330 | C12-C14 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 5-Oct | 2,94-3,70 | max. 0,1 | max.1* |
| CHS-EPOXY® RR 700 | 1, 6-hexanediol diglycidyl ether | Excellent reactivity at low temperatures and good solvent resistance, high mechanical strength, limited acid resistance | 15-25 | 6,70-7,20 | max. 0,2 | max.1* |
| CHS-EPOXY® RR 300 | Polypropyleneglycol diglycidyl ether | Flexibilizer, low toxicity and vapour pressure, reduced reactivity, limited diluting power | 40-90 | 2,90-3,30 | max. 0,3 | max.2* |
| CHS-EPOXY® RR 430 | C8-C10 alkyl glycidyl ether | Low toxicity and vapour pressure, good diluting power, reduced reactivity | 1-Jun | 4,25-4,55 | max. 0,05 | max.1* |
| Produkt | Description | Application | Viscosity (mPa) | Amino number | HEW |
|---|---|---|---|---|---|
| TELALIT® 2433 VBG 50 | Polyamine adduct modified (substitution for TELALIT® 180) | Waterborne systems | 1000-2000 | 130-150 | 243 |
| TELALIT® 95 | Cycloaliphatic adduct modified | Self-levelling flooring | 170-400 | 300-500 | 95 |
| TELALIT® 0600 | Cycloaliphatic, modified | High performance composites, long pot life, highest Tg | 80-100 | 450-500 | 62 |
| TELALIT® 0842 | Solvent free system, under water curing | Hardening in wet conditions, applicable in different weather conditions. | 1 100-1 900 | min.290 | 84 |
| TELALIT® 0590 | Polyoxyetheramine | Composites, long pot life | 5-Oct | 440-490 | 59 |
| TELALIT® 0846 | Mannich base without phenol (substitution for TELALIT® 60) | Universal hardener for epoxy systems, applicable in lower temperatures, unsuitable for food, beverages and drinking water | 550-750 | 345-375 | 84 |
| TELALITE® 1203 NF | Cycloaliphatic adduct, modified | For high solid coatings, nonyl phenol free | 50-400 | 250-300 | 120 |
| TELALIT® 0903 | Cycloaliphatic adduct modified | Self-levelling flooring, nonylphenol free, low yellowing | 200-500 | 320-350 | 90 |
| TELALIT® 3509 IX 50 | Aliphatic adduct modified (substitution for TELALIT® 160) | Lacquers, anticorrosive coatings | 200-700 | 110-135 | 350 |
| TELALIT® 1040 | Polyoxyetheramine | Waterborne coatings, high solid coatings, nonylphenol free. | Oct-30 | 230-260 | 104 |
| TELALIT® 0430 | Cycloaliphatic amine | Composites, civil engineering, faster curing, higher toughness | May-50 | 1250-1320 | 43 |
| TELALIT® 0492 | Cycloaliphatic modified | Composites, civil engineering | 15-30 | 550-600 | 49 |
| TELALIT® 0240 | Aliphatic amine (substitution for HARDENER P 11) | Standard, civil engineering, composites, adhesives | 5-Oct | 24 | |
| TELALIT® 0500 | Cycloaliphatic amine | Composites, accelerated | May-50 | 1100-1200 | 50 |
| TELALIT® 0420 | Cycloaliphatic amine | Composites, higher Tg | Oct-25 | 600-650 | 42 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
| VEROBOND® 531-0903 | Epoxy adhesive with low viscosity, cured at room temperature | Optimal for chemical anchors | A/B | 100/50 |
| VEROBOND® 14 | Epoxy adhesive or casting systems, cured at room temperature. Systems is a thixotropic paste adhesive of high strength with good chemical resistance | Adhesive for various type of materials | A/B | 100/50 |
| VEROBOND® QUICK | Unique, very fast epoxy adhesive (5 minutes curing time). | Universal adhesive for various type of materials | A/B | 100/100 |
| VEROBOND® 15 | Hybrid epoxy structural adhesive with high elongation and excellent peel and shear strengths | Adhesive for various type of materials | A/B | 100/100 |
| VEROBOND® SUPER | Adhesive with excellent shear and peel strenght, resistant up to 85°C | Universal adhesive for various type of materials, including thermoplastics and composites | A/B | 100/100 |
| VEROBOND® 520-2608 | High toughness, excellent peel streght, resistance up to 95°C | Universal adhesive for various type of materials, including thermoplastics and composites | A/B | 100/140 |
| CHS-EPOXY® 324 | Special phthalate-free epoxy system for adhesive composition and construction sealant | For standard temperatures, good chemical resistance | 100/7 | |
| CHS-EPOXY® 324 | Standard system, higher viscosity, balanced shear and peel strenght, resistant up to 60°C | Adhesive for metal, wood, glass | 100/11 | |
| CHS-EPOXY® 512 | Epoxy bonding agent for fixing of metal parts into mortar constructions | For standard temperatures & higher chemical resistance | 100/10 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
| VEROBOND® 531-0903 | Epoxy adhesive with low viscosity, cured at room temperature | Optimal for chemical anchors | A/B | 100/50 |
| VEROBOND® 14 | Epoxy adhesive or casting systems, cured at room temperature. Systems is a thixotropic paste adhesive of high strength with good chemical resistance | Adhesive for various type of materials | A/B | 100/50 |
| VEROBOND® QUICK | Unique, very fast epoxy adhesive (5 minutes curing time). | Universal adhesive for various type of materials | A/B | 100/100 |
| VEROBOND® 15 | Hybrid epoxy structural adhesive with high elongation and excellent peel and shear strengths | Adhesive for various type of materials | A/B | 100/100 |
| VEROBOND® SUPER | Adhesive with excellent shear and peel strenght, resistant up to 85°C | Universal adhesive for various type of materials, including thermoplastics and composites | A/B | 100/100 |
| VEROBOND® 520-2608 | High toughness, excellent peel streght, resistance up to 95°C | Universal adhesive for various type of materials, including thermoplastics and composites | A/B | 100/140 |
| CHS-EPOXY® 324 | Special phthalate-free epoxy system for adhesive composition and construction sealant | For standard temperatures, good chemical resistance | 100/7 | |
| CHS-EPOXY® 324 | Standard system, higher viscosity, balanced shear and peel strenght, resistant up to 60°C | Adhesive for metal, wood, glass | 100/11 | |
| CHS-EPOXY® 512 | Epoxy bonding agent for fixing of metal parts into mortar constructions | For standard temperatures & higher chemical resistance | 100/10 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
| EPOSTYL® 521-01 AS | Solvent-free epoxy system | Pigmented self-levelling flooring system, chemically resistant and antistatic. Suitable for interior. | A/B | 100/30 |
| EPOSTYL® 521 FLEX | Natural rubber epoxy system with excellent ductility above 70% and stratch resistance | Self-levelling and gravelled flooring and coatings for covering of cracks, for garages and interiors | A/B | 100/72 |
| EPOSTYL® 521-180 AS | Water-based epoxy system | Pigmented electro conductive coating for antistatic flooring | A/B | 100/400 //6 |
| EPOSTYL® GRANITE | Solvent-free epoxy system, excellent appearance | High decorative epoxy self-levelling flooring system-granite design | A/B/C | 70/30/150 |
| EPOSTYL® 521-01 | Solvent-free epoxy system. Different colours upon request (based on RAL). | Universal pigmented epoxy self-levelling flooring system | A/B | 100/30 |
| EPOSTYL® 521-01 | Solvent-free epoxy system. Different colours upon request (based on RAL). | Universal pigmented epoxy self-levelling flooring system | A/B | 100/30 |
| CHS-EPODUR® STONE UV | Special epoxy system for stone carpets, improved UV stability | Pavements, flooring | A/B | 100/43 //7 |
| CHS-EPODUR® STONE GEL | Special thixotropic epoxy system for finishing stone carpet | Stone carpet finishing gel | A/B | 100/40 |
| CHS-EPODUR® STONE | Special epoxy system for stone carpets | Pavements, flooring | A/B | 100/43 //7 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
| EPOSTYL® 521-01 AS | Solvent-free epoxy system | Pigmented self-levelling flooring system, chemically resistant and antistatic. Suitable for interior. | A/B | 100/30 |
| EPOSTYL® 521 FLEX | Natural rubber epoxy system with excellent ductility above 70% and stratch resistance | Self-levelling and gravelled flooring and coatings for covering of cracks, for garages and interiors | A/B | 100/72 |
| EPOSTYL® 521-180 AS | Water-based epoxy system | Pigmented electro conductive coating for antistatic flooring | A/B | 100/400 //6 |
| EPOSTYL® 521-01 | Solvent-free epoxy system. Different colours upon request (based on RAL). | Universal pigmented epoxy self-levelling flooring system | A/B | 100/30 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
| CHS-EPODUR® STONE UV | Special epoxy system for stone carpets, improved UV stability | Pavements, flooring | A/B | 100/43 //7 |
| CHS-EPODUR® STONE GEL | Special thixotropic epoxy system for finishing stone carpet | Stone carpet finishing gel | A/B | 100/40 |
| CHS-EPODUR® STONE | Special epoxy system for stone carpets | Pavements, flooring | A/B | 100/43 //7 |
| Produkt | Description | Application | Components | Mixing ratio |
|---|---|---|---|---|
| EPOSTYL® GRANITE | Solvent-free epoxy system, excellent appearance | High decorative epoxy self-levelling flooring system-granite design | A/B/C | 70/30/150 |
| EPOSTYL® 521-01 | Solvent-free epoxy system. Different colours upon request (based on RAL). | Universal pigmented epoxy self-levelling flooring system | A/B | 100/30 |
You can also find a comprehensive range of products in the product catalogue (PDF).
If you require detailed product information, please do not hesitate to contact us.